Super Hard 2000 Series 2024 10mm Anodized Aluminum Hex Bar Rod for Truck Wheel

Item

2024 10mm Anodized Aluminum Hex Bar Rod

Grade

1060,1100,1200,2024,2124,2014,2124,3003,3006,3030,5052,
5083,5154,5454,5754,5005,5652,6061,6062,6063,7075,etc

Standard

GB/T3191-1998,ASTM B221M-05A,JIS H4040-2006,etc

Diameter

2-250mm

Length

2m,3m,5.8m,6m,or as required

Finish Condition

O,H14,H12,H16,H18,H22,H112,T5,T6,T651,T351,T42,T451,T62,T3,T81,etc

Surface

Mill finish, polished, anodizing, ,powder coating, etc

Package

Standard export package ,or as required

Application

2024 aluminum hex bar rods are high strength hard aluminum, can be heat treatment
to strengthen, in the quenching and quenching state of plastic medium, spot
welding is good, with gas welding when the tendency to form intergranular
cracks, the alloy in the quenching and cold hardening after its Cutting
performance is good, after annealing can be low machinability: corrosion
resistance is not high, often using anodizing and coating method or surface
coated with aluminum layer to improve its corrosion resistance.
Mainly used to make a variety of high-load parts and components (but not
including stamping parts forging) such as aircraft on the skeleton parts, skin,
frame, ribs, spars, rivets and other working parts below 150℃.

Chemical Composition

Grade

Si

Fe

Cu

Mn

Mg

Cr

Ni

Zn

Ti

Zr

Al

2024

0.5

0.5

3.8-4.9

0.3-0.9

1.2-1.8

0.1

—

0.25

0.15

—

Balance

Mechanical Properties

Grade

Temper

Thickness(mm)

Tensile Strength(Mpa)

Yield strength(Mpa)

Elongation(%)

2024

T4

5-85

≥500

≥315

≥10